Two-Steps Versus One-Step Solidification Pathways of Binary Metallic Nanodroplets

Diana Nelli (1) , El Yakout El Koraychy (1) , Manuella Cerbelaud (2) , Benoit Crespin (3) , Arnaud Videcoq (2) , Alberto Giacomello (4) , Riccardo Ferrando (1)

1 UniGe - Università degli studi di Genova = University of Genoa
2 IRCER-AXE1 - IRCER - Axe 1 : procédés céramiques
3 XLIM-ASALI - Synthèse et analyse d'images
4 UNIROMA - Università degli Studi di Roma "La Sapienza" = Sapienza University [Rome]

The solidification of AgCo, AgNi, and AgCu nanodroplets is studied by molecular dynamics simulations in the size range of 2−8 nm. All these systems tend to phase separate in the bulk solid with surface segregation of Ag. Despite these similarities, the simulations reveal clear differences in the solidification pathways. AgCo and AgNi already separate in the liquid phase, and they solidify in configurations close to equilibrium. They can show a two-step solidification process in which Co-/Ni-rich parts solidify at higher temperatures than the Ag-rich part. AgCu does not separate in the liquid and solidifies in one step, thereby remaining in a kinetically trapped state down to room temperature. The solidification mechanisms and the size dependence of the solidification temperatures are analyzed, finding qualitatively different behaviors in AgCo/AgNi compared to AgCu. These differences are rationalized by an analytical model.

Domains: Physics [physics]

Diana Nelli, El Yakout El Koraychy, Manuella Cerbelaud, Benoit Crespin, Arnaud Videcoq, et al.. Two-Steps Versus One-Step Solidification Pathways of Binary Metallic Nanodroplets. ACS Nano, 2023, 17 (1), pp.587-596. ⟨10.1021/acsnano.2c09741⟩. ⟨hal-04262584⟩